High Speed Steel –M2 with good quality and high hardness
Heat Treatment of M2 Steel HSS
- Anneal
Heat to 1600° F, soak thoroughly at heat. Furnace cool 25° F per hour to 900° F, air cool to room temperature. Approximate annealed hardness 241 Maximum Brinell.
Stress Relief of Unhardened Material: Heat slowly to 1200 to 1250° F. Soak for two hours per inch of thickness at heat. Slow cool (furnace cool if possible) to room temperature.
- Harden
Heat slowly to 1550° F, soak thoroughly, heat to 1850° F, soak thoroughly. Soak time in the furnace varies from a few minutes to 15 minutes, depending tool size, heat capacity of the furnace, and the size of the charge. – Heat to 2150 to 2200° F for max. toughness and minimum distortion. – Heat to 2250 to 2275° F for max. hardness and abrasion resistance.
- Quench
For full hardness, oil quench to 150-200° F. Air quench to 150° F. When quenching in hot salt maintain the quench just above the Ms temperature. After equalizing withdraw parts from the hot salt and air cooled to 150° F.
- Temper
Double temper is mandatory, three tempers are sometimes preferred. Soak for 2 hours per inch of thickness. Air cool to room temperature between tempers. The best tempering range for hardness, strength and toughness is 1000 to 1050° F.
Machinability of AISI M2 Tool Steel H-SS
Shaping of HSS M2 tool steels can be carried out using grinding methods. However, they have poor grinding capability and hence they are regarded as “medium” machinability tool steel under annealed conditions. The machinability of these tool steels M2 is only 50% of that of the easily machinable W group or water hardening tool steels.
M2 Tool Steel Applications
The main use of high-speed steels continues to be in the manufacture of various cutting tools.
Typical applications for M2 high speed steel are twist drills, reamers, broaching tools, taps, milling tools, metal saws. M2 is suitable for cold forming tools such as extrusion rams and dies, also widely used in all kinds of cutting tools, knife and punches and die applications, plastic moulds with elevated wear resistance and screws.
Contact us for M2 tool steel price request. We are a better M2 steel tool material supplier for you.
Ms Florence Lin
Mobile/WhatsApp: 0086-13790538953
Tel: 0086-769-23190193
Fax: 0086-769-88705839
Email: Florence@otaisteel.com