X165CrMoV12 | 1.2601 Cold Work Alloy Tool Steel China suppliers, wholesale, distributors and stockholder. Otai Special Steel is manufacturers and Have large quantity Stock in warehouse.  We supply in Round bar, gauge plate steel, pipe / Tube,rod, square, hexagonal, blanks, plate, sheet, precision ground flat bar, precision ground bar stock and hollow bar. provide black surface and black surface alloy steel material.
X165CrMoV12 | 1.2601 is a German Cold work tool alloy steel material grade.it is shock resisting steel. it belong to DIN 17350 standard. Digital Grade material number 1.2601. Metal Steel Grade W-Nr X165CrMoV12  It is a die steel, use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cutting mold. Our Tool Steel material 100 % ultrasonic tested with good price. Small size steel products make by hot rolled, large size steel products make by forging. 1.2601 with X165CrMoV12 is equivalent Belong to W-Nr and DIN.

bright surface T15 steel bar

 X165CrMoV12 | 1.2601 Steel material properties datenblatt as below:
Chemical composition data of Metal X165CrMoV12 | 1.2601 Cold work tool steel-DIN 17350-1980 (EN4957-2001)
C Si Mn P S W Cr V
1.55～1.75 0.25～0.40 0.20～0.40 0.030 max 0.030 max 0.40～0.60 11.0～12.0 0.10～0.50
Material equivalent of DIN X165CrMoV12 | 1.2601 steel
USA Germany China Japan France England Italy Poland Czechia Austria Sweden Spain
AISI DIN,WNr GB JIS AFNOR BS UNI PN CSN ONORM SS UNE
X165CrMoV12 | 1.2601  X165CRMOW12KU  2310 X160CRMOV12
Physical properties of X165CrMoV12 | 1.2601 Tool Steel
  • Density: 7.85kg/m3
  • Thermal conductivity:
  • Forging ratio: 5:1 Minimum
  • Microstructure:
  • Magnetic:
Mechanical properties of Alloy Steel X165CrMoV12 | 1.2601

Hardness： Annealing  225 HB max, Q+T: 58-63 HRc, different hardness according different Tempering temperature.

  • Yield strength:

Heat treatment of X165CrMoV12 | 1.2601 Cold work tool steel

  • Annealing: Annealing temperature/℃: 800~830; After the annealing, degree of hardness ≤HBS: 255
  • Quenching: Hardening temperature/℃: 980~1010, Quenching in oil or air
  • Tempering: Commonly used drawing temperature/℃: 180~250;  After tempering hardness HRC | 100 ℃ : 63; After tempering hardness HRC | 200 ℃ : 61; After tempering hardness HRC | 300 ℃ : 60 ; After tempering hardness HRC | 400 ℃ : 58
  • Normalizing：at Normalizing temperature, then cool in furnace

 

Forged steel properties of Cold work tool X165CrMoV12 | 1.2601 tool steel

For forging  X165CrMoV12 | 1.2601 steel, Slowly Pre-heat, at  temperature/℃: 1050~850 Forged

Processing of Steel Material X165CrMoV12 | 1.2601

Otai Special provide the Grinding, milling , polishing, turning, drilling and others machining service as your required tolerances and size.

Packing of X165CrMoV12 | 1.2601 steel

By steel Wire Bundling then put in container, or as customer require packing.

Contact us now!  Free sample waiting for you.