1.2516 | 120WV4 Cold work tool Tool Steel China suppliers, wholesale,  distributors and stockholder. Otai Special Steel is manufacturers and Have large quantity Stock in warehouse.  We supply in Round bar, gauge plate steel, pipe / Tube,rod, square, hexagonal, blanks, plate, sheet, precision ground flat bar, precision ground bar stock and hollow bar. provide black surface and black surface alloy steel material.
1.2516 | 120WV4 is a German Cold work tool alloy steel material grade.it is shock resisting steel. it belong to DIN 17350 standard. Digital Grade material number W-Nr 1.2516 | 120WV4, Metal Steel garde X210CrW12.  It is a die steel, use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cast mold. Our Tool Steel material 100 % ultrasonic tested with good price. Small size steel products make by hot rolled, large size steel products make by forging. 1.24539 with X130W5 is equivalent Belong to W-Nr and DIN.

T1-high-speed-tool-steel

1.2516 | 120WV4 Steel material properties datenblatt as below:
Chemical composition data of Metal 1.2516 | 120WV4 Cold work tool steel-DIN 17350-1980 (EN4957-2001)
C Si Mn P S W Cr V
1.15～1.25 0.15～0.30 0.20～0.35 0.03 max 0.03 max 0.90～1.10 0.15～0.25 0.07～0.12
Material equivalent of DIN 1.2516 | 120WV4 steel
USA Germany China Japan France England Italy Poland Czechia Austria Sweden Spain
– DIN,WNr GB JIS AFNOR BS UNI PN CSN ONORM SS UNE
1.2516 | 120WV4
Physical properties of 1.2516 | 120WV4 Tool Steel
  • Density: 7.85kg/m3
  • Thermal conductivity:
  • Forging ratio: 4:1 Minimum
  • Microstructure:
  • Magnetic:

 

Mechanical properties of Alloy Steel 1.2516 | 120WV4
  • Hardness： Annealling  230 HB max, Q+T: 51-65 HRc, different hardness according different Tempering temperature.
  • Yield strength:

 

Heat treatment of  1.2516 | 120WV4 Cold work tool steel
  • Annealing: Annealing temperature/℃: 710~740; After the annealing, degree of hardness ≤HBS: 230
  • Quenching: Hardening temperature/℃: 780~810, Quenching in water
  • Tempering: Commonly used drawing temperature/℃: 180~250;  After tempering hardness HRC | 100 ℃ : 65; After tempering hardness HRC | 200 ℃ : 62; After tempering hardness HRC | 300 ℃ : 57 ; After tempering hardness HRC | 400 ℃ : 51
  • Normalizing：at Normalizing temperature, then cool in furnace

 

Forged steel properties of Cold work tool 1.2516 | 120WV4 tool steel

For forging 1.2516 | 120WV4 steel, Slowly Pre-heat, at  temperature/℃: 1050~850 Forged

Processing of Steel Material 1.2516 | 120WV4

Otai Special provide the Grinding, milling , polishing, turning, drilling and others machining service as your required tolerances and size.

Packing of 1.2516 | 120WV4 steel

By steel Wire Bundling then put in container, or as customer require packing.

Contact us now!  Free sample waiting for you.

Tel: 0086-769-33232622
Fax: 0086-769-88705839
Email: jack@otaisteel.com