HS6-5-2 Annealled Round Bar Qualified Sales Promotion After Coronavirus in China in March . This time Chinese Spring Festival holiday was very special . We did not use this holiday to party with all our relatives and friends as usual . In the end there was no travel to relax . Instead , we were stayed at home with close relatives . Due to the effects of the new coronavirus . We respond to government calls to isolate ourselves and prevent the spread of the virus . Our efforts have paid off. Most of us are now back to work .
In this month , our HS6-5-2 Annealled Round Bar Qualified have sales promotion to our regular customer . Thanks for all your pay attention to us . All of us hope the world are peaceful .
Otai Special Steel have HS6-5-2 Annealled Round Bar Qualified Sales Promotion After Coronavirus in China in March .
HS6-5-2 Annealled Round Bar Qualified Tool Steel Chemical Composition Properties
ASTM A600 | C | Mn | P | S | Si | Cr | V | Mo | W | |||||||
M2 regular C | 0.78 | 0.88 | 0.15 | 0.40 | 0.03 | 0.03 | 0.20 | 0.45 | 3.75 | 4.50 | 1.75 | 2.20 | 4.50 | 5.50 | 5.50 | 6.75 |
DIN ISO 4957 | C | Mn | P | S | Si | Cr | V | Mo | W | |||||||
1.3343 | 0.86 | 0.94 | … | … | … | … | … | 0.45 | 3.80 | 4.50 | 1.70 | 2.10 | 4.70 | 5.20 | 5.90 | 6.70 |
JIS G4403 | C | Mn | P | S | Si | Cr | V | Mo | W | |||||||
SKH51 | 0.80 | 0.88 | … | 0.40 | 0.03 | 0.03 | … | 0.45 | 3.80 | 4.50 | 1.70 | 2.10 | 4.70 | 5.20 | 5.90 | 6.70 |
HS6-5-2 Annealled Round Bar Qualified Mechanical Properties
- Physical Properties of HSS M2 (Corresponding materials )
Density | 0.294 lb/in3 (8138 kg/m3) |
Specific Gravity | 8.15 |
Modulus of Elasticity | 0.294 lb/in3 (8138 kg/m3) |
Thermal conductivity | 24 Btu/ft/hr/°F 41.5 W/m/°K |
Machinability | 65% of a 1% carbon steel |
- HS6-5-2 Annealled Round Bar Qualified Tool Steels Properties Mechanical
Mechanical properties | Metric | Imperial |
Hardness, Rockwell C (tempered at 1150°F, quenched at 2200°F) | 62 | 62 |
Hardness, Rockwell C (as hardened, quenched at 2200°F) | 65 | 65 |
Compressive yield strength (when tempered at 300°F) | 3250 MPa | 471000 psi |
Izod impact unnotched (when tempered at 300°F) | 67 J | 49.4 ft-lb |
Abrasion (loss in mm3, as-hardened; ASTM G65) | 25.8 | 25.8 |
Abrasion (loss in mm3, tempered at 1275°F; ASTM G65) | 77.7 | 77.7 |
Poisson’s ratio | 0.27-0.30 | 0.27-0.30 |
Elastic modulus | 190-210 GPa | 27557-30458 ksi |
- HS6-5-2 Annealled Round Bar Qualified Steels Thermal Properties
Thermal properties | Metric | Imperial |
CTE, linear (@20.0 – 100°C/ 68.0 – 212°F) | 10 μm/m°C | 5.56 μin/in°F |
CTE, linear (@20.0 – 500°C/68.0 – 932°F) | 12.2 μm/m°C | 6.78 μin/in°F |
CTE, linear (@20.0 – 850°C/68.0 – 1560°F) | 12.6 μm/m°C | 7 μin/in°F |
Forging of AISI M2 High Speed Steel (Corresponding materials )
Pre heat M2 HSS steel slowly and uniformly to 850-900°C. The heat should then be increased more quickly to the forging temperature of 1050-1150°C. If during the forging the temperature of the M2 high speed tool steel material drops below 880-900°C, re-heating will be necessary. Cool the M2 steel component very slowly after forging.
- Anneal
Heat to 1600° F, soak thoroughly at heat. Furnace cool 25° F per hour to 900° F, air cool to room temperature. Approximate annealed hardness 241 Maximum Brinell.
Stress Relief of Unhardened Material: Heat slowly to 1200 to 1250° F. Soak for two hours per inch of thickness at heat. Slow cool (furnace cool if possible) to room temperature.