O7 Steel Oil-Hardening Cold Work Tool Steel

O7 Tool steel is a cold work steel belong to ASTM A681-1999 Steel Grade standard. O7 Steel China Supplier and factory Otai Special Steel Supply O7 Cold Work Tool steel in Round bar, Plate, Flat bar, Square, Forging Ring and others any shape. And provide cutting, sawing, milled, machining processing.

AISI O7 cold work steel Data pdf

Supply Form of O7 -ASTM A681 Alloy Cold Work Tool Steel
Supply Range of aisi O7 Tool Steel

O7 Steel Round Bar: diameter 5mm – 400mm

O7 Steel Plate: thickness 10 –500mm x width 200– 1400mm

O7 Steel Block: 210mm x 500-810mm

O7 STEEL -ASTM AISI O7 TOOL STEEL BAR

Chemical Composition of O7 Tool Steel Material
ASTM A681 C Si Mn P S Cr Mo V W
O7/T31506  1.10～1.30  0.10～0.60 0.20～1.00  0.030 Max  0.030 Max 0.35～0.85  ≤0.30 ~0.15～0.40 1.00～2.00
DIN 17350 C Si Mn P S Cr Mo V
GB/T 1299 C Si Mn P S Cr Mo V
JIS G4404 C Si Mn P S Cr Mo V
O7 tool Steel Equivalent and Related Speciation
USA German Japan China ISO
ASTM A681 DIN 17350 JIS G4404 GB/T 1299 ISO 4957
O7

 

ASTM AISI O7 Tool Steel Material Mechanical Properties

Hardness, Rockwell C: 65 HRc, Density: 7.67kg/m3

Izod impact unnotched: .

Melting point:

Thermal expansion: 12.48 mm/m°C (25-250 ºC)

Elastic modulus:     190-210 GPa (at 25 ºC ).

Forged of Cold Work Steel O7 material metal

Forged O7 tool steel at 820-1070 ºC. no forging when below 800 ºC.

Heat Treatment of SAE/AISI O7 Steel
  • O7 Steel Annealing

Slowly heat to 790 ºC, keep enough time, ensure heat thoroughly. then cooling in furnace at 4-5 ºC per hour. After annealing, the hardness 217 HBS Max.

  • O7 tool Steel Hardening & Quenching

/ ℃ quenching temperature: 790～840

Quenching medium: oil

  • Tempering Of O7 Steel

/ ℃ tempering temperature: 150 ~ 320

After tempering hardness HRC: 63-58

Application of Sae AISI O7 tool Steel

O7 tool steel used for cold work tool products. Like stamping die, paper cutter appliances.

Quality Assured of Sae O7 Steel

Quality assured by Our ISO 9001:2008 quality management system. Our all O7 tool steel all had by SEP 1921-84 ultrasonic inspection (UT Test). Quality Grade: E/e, D/d, C/c.

If you have any O7 steel inquiry and question for Price, Application, hot treatment, please don’t hesitate to contact us.