M42 Tool Steel | SKH59 | HS 2-9-1-8 | 1.3247 High Speed Steel
SAE M42 Tool Steel is high cobalt high speed steel. And High Speed Steel toughness and is mainly used for high toughness precision wear-resistant metal cold die.Moreover it also can be used for the cutting tool and the knife in the cooling. M42 HIGH SPEED STEEL PDF DOWN
Supply Form of M42 Tool Steel -ASTM A681 High Speed Steel
Supply Range of SAE M42 Tool Steel
M42 Steel Round Bar: diameter 1mm – 400mm
M42 Steel Plate: thickness 1 –500mm x width 200– 1400mm
M42 Steel Block: 210mm x 500-810mm
Chemical Composition of M42 Tool Steel Material
ASTM A681 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
M42/ T11342 | 1.05~1.15 | 0.15~0.65 | 0.15~0.40 | 0.030 Max | 0.030 Max | 3.50~4.25 | 9.00~10.00 | 0.95~1.35 | 1.15~1.85 | 7.75~8.75 |
DIN 17350 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
1.3247/S2-10-1-8 | 1.05~1.15 | ≤0.70 | ≤0.40 | 0.030 Max | 0.030 Max | 3.50~4.50 | 9.00~10.00 | 0.90~1.30 | 1.20~1.90 | 7.50~8.50 |
GB/T 1299 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
W2Mo9Cr4VCo8 | 1.05~1.15 | 0.15~0.65 | 0.15~0.40 | 0.030 Max | 0.030 Max | 3.50~4.25 | 9.00~10.00 | 0.95~1.35 | 1.15~1.85 | 7.75~8.75 |
JIS G4403 | C | Si | Mn | P | S | Cr | Mo | V | w | Co |
SKH59 | 1.05~1.15 | ≤0.70 | ≤0.40 | 0.030 Max | 0.030 Max | 3.50~4.50 | 9.00~10.00 | 0.90~1.30 | 1.20~1.90 | 7.50~8.50 |
M42 Tool Steel Material Equivalent and Related Speciations
USA | German | Japan | China | ISO |
ASTM A681 | DIN 17350 | JIS G4403 | GB/T 1299 | ISO 4957 |
M42 | 1.3247 | SKh59 | W2Mo9Cr4VCo8 | HS 2-9-1-8 |
SAE M42 Tool Steel Material Mechanical Properties
Hardness, Rockwell C (oil quenched on 1204°C, 5 minutes): 63 HRC.
Hardness, Rockwell C (oil quenched on 1177°C, 5 minutes): 65.5 HRC
Hardness, Rockwell C(oil quenched on 1163°C), 5 minutes: 65.8 HRC
Forged of M42 Steel metal material
At first, Pre-Heating to 650-750℃,Then heat to forged temperature. Next, Soak at 1050-1100 °C , ensure heat thorough. Then start forged, the forged temperature no low than 950℃. After forging, cool slowly .
Heat Treatment of SAE M42 Steel
- M42 HSS Steel Annealing
Firstly, Slowly heat to 870℃,then slowly Cool to 538℃(1000℉) in heat treatment furnace. Then cool in air. After annealing hardness HBS: 269 Max
- M42 tool Steel Hardening
M42 steel having very high hardenability and should be hardened by cooling in still air. The use of a salt bath or controlled atmosphere furnace is desirable to minimize decarburization, and if not available, pack hardening in spent pitch coke is suggested. Finally, the temperature employed is usually 1800°-1850°F, depending on size section.
- Quenching of HSS M42 Steel material
Quenching temperature / ℃ | salt bath furnace: 1177
Quenching temperature / ℃ | controlled atmosphere furnace: 11188
The heat preservation time/min: 5 ~ 15
Quenching medium: air cooling
- Tempering Of HSS M42 Tool Steel
Tempering temperature / ℃ : 538
After tempering hardness HRC or higher: 66
Application of Sae M42 tool Steel HSS
Suitable for manufacturing various strong cutting tools with wear-resistant, resistant to impact. Advanced punching die, screw die, the toughness and complicated shape of the punch, etc. Roll cutting tool industry: scraper, serrated knife, iron knives, drill bits, etc.
Forging industry: forging die.
Screw industry: heading forming mould, such as teeth, punch
Quality Assured of Sae M42 Steel
Quality assured by ISO 9001:2008 quality management system. Whatsmore, Our all M42 tool steel all had by SEP 1921-84 ultrasonic inspection (UT Test). Quality Grade: E/e, D/d, C/c.
If you have any M42 Tool steel inquiry and question for Price, Application, hot treatment, Please don’t hesitate contact us.