1.2436 Cold work tool Tool Steel China suppliers, wholesale, distributors and stockholder. Otai Special Steel is manufacturers and Have large quantity Stock in warehouse. We supply in Round bar, gauge plate steel, pipe / Tube,rod, square, hexagonal, blanks, plate, sheet, precision ground flat bar, precision ground bar stock and hollow bar. provide black surface and black surface alloy steel material.
1.2436 is a German Cold work tool alloy steel material grade.it is shock resisting steel. it belong to DIN 17350 standard. Digital Grade material number W-Nr 1.2436, Metal Steel garde X210CrW12. It is a die steel, use in extrusion moulds, Hot Cast moulds. like aluminium production, Aluminium cast mold. Our Tool Steel material 100 % ultrasonic tested with good price. Small size steel products make by hot rolled, large size steel products make by forging.
1.2436 Steel material properties datenblatt as below:
Chemical composition data of Metal 1.2436 Cold work tool steel-DIN 17350-1980 (EN4957-2001)
| C | Si | Mn | Ni | P | S | W | Cr |
| 2.00-2.25 | 0.10-0.40 | 0.15-0.45 | 1.5 – 1.8 | 0.03 max | 0.03 max | 0.60-0.80 | 11.0～12.0 |
Material equivalent of DIN 1.2436 steel
| USA | Germany | China | Japan | France | England | Italy | Poland | Czechia | Austria | GOST | Inter |
| – | DIN,WNr | GB | JIS | AFNOR | BS | UNI | PN | CSN | ONORM | GOST | ISO |
| D3 | X210CrW12 | Cr12W | SKD2 | X210CrW12-1 | X210CrW12 | ||||||
Physical properties of 1.2436 Tool Steel
- Density: 7.85kg/m3
- Thermal conductivity:
- Forging ratio: 4:1 Minimum
- Microstructure:
- Magnetic:
Mechanical properties of Alloy Steel 1.2436
- Hardness： Annealling 255 HB max, Q+T: 58-38HRc, different hardness according different Tempering temperature.
- Yield strength:
Heat treatment of （55NiCrMoV7） 1.2436 Cold work tool steel
- Annealing: Annealing temperature/℃: 800~830; After the annealing, degree of hardness ≤HBS: 255
- Quenching: Hardening temperature/℃: 930~980, Quenching in water
- Tempering: Commonly used drawing temperature/℃: 180~250; After tempering hardness HRC | 100 ℃ : 63; After tempering hardness HRC | 200 ℃ : 62; After tempering hardness HRC | 300 ℃ : 60 ; After tempering hardness HRC | 400 ℃ : 58
- Normalizing：at Normalizing temperature, then cool in furnace
Forged steel properties of Cold work tool 1.2436 tool steel
For forging 1.2436 steel, Slowly Pre-heat, at Hot-working temperature/℃: 1050~850
Processing of Steel Material 1.2436 | 56NiCrMoV7
Otai Special provide the Grinding, milling , polishing, turning, drilling and others machining service as your required tolerances and size.
Packing of 1.2436 steel
By steel Wire Bundling then put in container, or as customer require packing.